Polymer1 | KHN | FT [MPa·m0.5] | Abrasion [nm·cycle−1] | Attrition [nm·cycle−1] |
Arm number (SH) | ||||
3-star | 58.9 (3.5)a, 2 | 1.05 (0.06)c | 0.41 (0.12) | 0.71 (0.06)f |
4-star | 58.5 (0.6)a | 1.11 (0.18)c | 0.26 (0.05)e | 0.73 (0.20)f |
6-star | 51.4 (4.3) | 1.06 (0.13)c | 0.26 (0.07)e | 1.29 (0.32) |
Branching (SH) | ||||
LDB | 58.5 (0.6) | 1.11 (0.18)d | 0.26 (0.05) | 0.73 (0.20) |
MDB | 49.2 (1.4)b | 1.11 (0.22)d | 0.32 (0.06) | 0.92 (0.15) |
HDB | 50.2 (1.4)b | 1.08 (0.13)d | 0.56 (0.18) | 1.31 (0.30) |